The Performance of the Titania Ceramic Membrane for Desalination

Authors： JIANG Lin，MA Wei，CHEN Zhi*，LI Jian-ming

Units： School of Chemical Engineering, Sichuan University, Chengdu 610065, China

KeyWords： TiO2 ceramic membrane; membrane distillation; permeation flux; desalination rate

ClassificationCode：TQ051.8+93

year,volume(issue):pagination： 2013,33(3):28-32

Abstract：

The orthogonal experiments of air gap membrane distillation (AGMD) with three factors and four levels were carried out to seek the best operation condition which considered the indexes of the permeation flux and the desalination rate. The effects of operating conditions, such as operating temperature, concentration of the NaCl solution, and feed flow rate on the indexes and desalination efficiency of the membrane were also investigated. It is shown, from the range and variance analyses of the experimental results, that the permeation flux is significantly affected by the operating temperature, but slightly affected by the concentration of the NaCl solution, and the permeation flux increases with the increasing operating temperature and feed flow rate. At the same time, the desalination rate is significantly affected by the operating temperature, but slightly affected by the feed flow rate, and the desalination rate decreases with the increasing operating temperature and the concentration. From all above, the conclusions could be following: the operating temperature must be determined as a proper value based on the balance between the energy consumption and the water throughput according to the practical conditions; the membrane prepared gets better desalination efficiency for 2% NaCl solution than the other concentration’s; the increase of the feed flow rate would result in the increasing permeation flux, which is benefit for the water throughput.

Funds：

AuthorIntro：

作者简介：蒋琳（1988–），男，四川绵阳人，硕士研究生，主要研究方向为过滤与分离。 * 通讯联系人，E-mail：chenzhi_hx@scu.edu.cn

Reference：

[1] 杨兰. 用气隙式膜蒸馏进行膜渗透性能影响因素研究[J]. 齐齐哈尔大学学报, 2002, 18(3): 1－4.
[2] A. Ayral, L. Cot, J. Durand, C. Guizard, N. Hovnanian, A. Jube, A. Larbot. Inorganic membranes and solid state sciences [J]. Solid State Sci., 2000, 2: 313－334.
[3] 朱长乐. 膜科学技术[M]. 北京：高等教育出版社, 2004.
[4] 潘艳秋，余雅兰等. 真空膜蒸馏NaCl水溶液脱盐过程模拟研究[J]. 大连理工大学学报, 2010, 50(3): 328－333.
[5] 涂正环, 贺高红等. 减压膜蒸馏法咸水淡化的实验研究[J]. 海湖盐与化工, 2003, 32(5): 10－14.
[6] 高振, 朱春英等. 真空膜蒸馏过程影响因素研究[J]. 海湖盐与化工, 2004, 34(1): 10－13.
[7] 边文兵, 武春瑞, 吴丹等. 减压膜蒸馏法稀碱液浓缩过程研究[J]. 水处理技术, 2010, 36(1): 44－47.
[8] 丁忠伟, 李兆曼等. 气扫式膜蒸馏用于脱除水中氨的分离性能[J]. 北京化工大学学报, 2007, 34(1): 5－8.
[9] 王车礼, 王军等. 减压膜蒸馏浓缩NaCl溶液的实验研究[J]. 海湖盐与化工, 2002, 32(2): 8－10.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com