Preparation of nitrogen-doped mesoporous carbon materials from oligoimide precursors

Authors： LIU Yuanyuan1,2, HAYAKAWA Teruaki2, WANG Xiaolin1

Units： 1. Beijing Key Laboratory of Membrane Materials and Engineering, Department of Chemical Engineering, Tsinghua University, Beijing 100084, China; 2. Department of Organic and Polymeric Materials, Tokyo Institute of Technology, Tokyo 152-8552, Japan

KeyWords： oligoimides; nitrogen-doped mesoporous carbon; high regularity; morphology control

ClassificationCode：O631.1

year,volume(issue):pagination： 2014,34(5):33-39

Abstract：

Well-ordered nitrogen-dopedmesoporous carbon materials were prepared via a soft-templating method by using block copolymers as the template, oligoimide as the nitrogen source and crosslinked phenolic resin as the carbon source, through successive steps of self-assembly, crosslinking, and heat treatment. FT-IR, SEM, TEM, thermogravimetric analysis and small angle x-ray diffraction were used to characterize the constitution and mesostructures of obtained materials. The results indicated that the block copolymer templates were successfullyremoved at 350 ℃ to generate porous structures, and at a higher temperature of 600 ℃, the matrix consisting of oligoimides and crosslinked phenolic resin will carbonize to form the nitrogen-doped mesoporous carbons with high regularity. Since carbon and nitrogen precursors selectively dissolve in the hydrophilic phase formed by the block copolymer templates and change the hydrophilic/hydrophobic ratios, the morphologies of the newly developed carbon materials can be finely tuned by adjusting the ratios of each component in the system, and numerous morphologies, including sphere, cylinder and lamellar can be obtained.

Funds：

国家高技术研究发展计划(863)项目(批准号：2012AA03A604)

AuthorIntro：

刘圆圆(1989-)，女，福建人，博士研究生，主要研究方向为规整结构新型膜的制备及研究，联系电话：010-62794742，E-mail: liuyuanyuan07@gmail.com **通讯作者：E-mail：xl-wang@tsinghua.edu.cn.

Reference：

[1] Deng Y, Wei J, Sun Z,et al. Large-pore ordered mesoporousmaterials templated from non-pluronicamphiphilicblock copolymers[J]. ChemSoc Rev, 2013, 42: 4054-4070.
[2] Li W, Zhao D. An overview of the synthesis of orderedmesoporousmaterials[J]. ChemCommun, 2013, 49: 943-946.
[3] Fang Y,Lv Y,Che R, et al. Two-dimensional mesoporouscarbon nanosheets and their derived graphenenanosheets: synthesis and efficient lithium ion storage[J]. J Am ChemSoc, 2013, 135: 1524-1530.
[4] Xue C,Lv Y, Zhang F,et al. Copper oxide activation of soft-templatedmesoporouscarbons and their electrochemical properties for capacitors[J]. J Mater Chem, 2012, 22: 1547-1555.
[5] Wu D, Xu F, Sun B, et al. Design and preparation of porous polymers[J]. Chem Rev, 2012, 112: 3959-4015.
[6] WeiJ, ZhouD, SunZ, et al. A controllable synthesis of rich nitrogen-doped ordered mesoporouscarbon for CO2capture and supercapacitors[J]. AdvFunct Mater, 2013, 23: 2322-2328.
[7] ChenH, SunF, Wang J, et al. Nitrogen doping effects on the physical and chemical properties of mesoporouscarbons[J]. J PhysChem C, 2013, 117: 8318-8328.
[8] Ryoo R,Joo S H, Kruk M, et al. Ordered mesoporouscarbons[J]. Adv Mater, 2001, 13: 677-681.
[9] Kim T W, Park I S,Ryoo R. A synthetic route to ordered mesoporouscarbon materials with graphitic pore walls[J]. AngewChem, 2003, 115: 4511-4515.
[10] Lu A, Kiefer A, Schmidt W, et al. Synthesis of polyacrylonitrile-based ordered mesoporouscarbon with tunable pore structures[J]. Chem Mater, 2004, 16: 100-103.
[11] Talapaneni S N,Anandan S, Mane G P,et al. Facile synthesis and basic catalytic application of 3D mesoporouscarbon nitride with a controllable bimodal distribution[J]. J Mater Chem, 2012, 22: 9831-9840.
[12] Yang W,Fellinger T P,Antonietti M. Efficient metal-free oxygen reduction in alkaline medium on high-surface-area mesoporousnitrogen-doped carbons made from ionic liquids and nucleobases[J]. J Am ChemSoc, 2011, 133: 206-209.
[13] Shrestha S,Mustain W E. Properties of nitrogen-functionalized ordered mesoporouscarbon prepared using polypyrroleprecursor[J]. J ElectrochemSoc, 2010, 157: B1665-B1672.
[14] Xia Y, Mokaya R. Synthesis of ordered mesoporouscarbon and nitrogen-doped carbon materials with graphitic pore walls via a simple chemical vapor deposition method[J]. Adv Mater, 2004, 16: 1553-1558.
[15] Datta K K R,Balasubramanian V V,Ariga K, et al. Highly crystalline and conductive nitrogen-doped mesoporouscarbon with graphitic walls and its electrochemical performance[J]. ChemEur J, 2011, 17: 3390-3397.
[16] Liu R, Wu D, Feng X, et al. Nitrogen-doped ordered mesoporousgraphitic arrays with high electrocatalyticactivity for oxygen reduction[J]. AngewChem, Int Ed, 2010, 49: 2565-2569.
[17] Liang C, Hong K,Guiochon G A, et al. Synthesis of a large-scale highly ordered porous carbon film by self-assembly of block copolymers[J]. AngewChem, Int Ed, 2004, 43: 5785-5789.
[18] Liang Y, Fu R, Wu D. Reactive template-induced self-assembly to ordered mesoporouspolymeric and carbonaceous materials[J]. ACS Nano, 2013, 7: 1748-1754.
[19] Meng Y,Gu D, Zhang F,et al. A family of highly ordered mesoporouspolymer resin and carbon structures from organic-organic self-assembly[J]. Chem Mater, 2006, 18: 4447-4464.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com