Sulphuration of PPS non-woven felt thin film by chlorosulfonic acid and characterization

Authors： XU Zhi cheng,WANG Le yi,ZHANG Wei Zheng,ZHAO Yue xuan,

Units： Shandong Zhaojin Motian co.,LTD, Zhaoyuan,265400,China

KeyWords： PPS；sulphuration；hydrophilic property

ClassificationCode：TQ320.721

year,volume(issue):pagination： 2016,36(5):68-71

Abstract：

The hydrophilic property of PPS non—woven felt thin film was improved by using sulphuration.The effects of time，temperature and the ratio of reactants on the property of hydrophilic of PPS were illustrated in detail．The introduction of —SO3H to sulphurated PPS was characterized by FTIR spectroscopy and Energy Dispersive X-ray (EDX). The result shows that not only the hydrophilic property of PPS non—woven felt is excellently improved but also the original stretch intensity of PPS non—woven felt thin film is well retained when the sulphuration temperature is 80℃ and time is 1.5 h．

Funds：

国家科技支撑计划（2014BAK13B02）

AuthorIntro：

作者简介：徐志成（1980-），男，山东潍坊市人，硕士研究生，工程师，从事高分子膜制备与应用方向研究；电子邮件：chenggong-2100@163.com

Reference：

[1]郭振华，对我国PPS开发之我见[J]．化工新型材料，1995，(5)：26—30．
[2]富醇熹．双向拉伸PPS薄膜[J]．化工新型材料，1993，(2)：36，38．
[3]陈贻炽．聚苯硫醚的合成及性能[J]．化工新型材料，1994，(8)：2l一24．
[4]张念萱，刘皓颖．PPS双向拉伸膜发展概况[j]．北京化工，1994，(3)：l3一l7．
[5] 余建佳，李飞，周璇. 磺化聚苯醚的制备[J],胶体与聚合物,2005,23：22-23
[6]陈雷,张俊,杨昌正等. 磺化SBS 薄膜的制备与表征[J]，功能高分子学报,1998 ,11(1):39-43.
[7]吕亮,许青青.废旧聚苯乙烯磺化反应研究[J],天津化工,2002,5：11-12.
[8]韦异,陈薇,赵文锋等.SBS的磺化改性[J],精细石油化工,2002,5：23-25.
[9]KIMIC,TAKTM,CHOIJG.Sulfonated polyether-sulfone by heterogeneous method and its membraneperformances[J],J Appl Polym Sci,1999,74(8)：2046- 2055.
[10]项昭保,霍丹群,候长军等.聚醚砜的磺化改性[J],重庆大学学报,2002,25(10)：117-120.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com