Research on Properties of Al2O3-ZrO2 Composite Membrane with Different Molar Ratios
Authors: WANG Jiayue,TONG Zhi,GAO Tingting,LIU Ting
Units: School of Environmental and Chemical Engineering,Xi’an Polytechnic University,Xi’an 710048,China
KeyWords: Al2O3;ZrO2;Al2O3-ZrO2 Composite Membranes;Viscosity;Crystal phase transition
ClassificationCode:X781.5
year,volume(issue):pagination: 2018,38(6):84-89

Abstract:
Using Al2O3 sol and ZrO2 sol with different molar ratio(r),Al2O3-ZrO2 composite membranes were prepared by sol-gel method.The results of the characterized analysis which use testing instruments such as Ukrainian viscosity,thermogravimetric(TG-DTG),Fourier transform infrared(FT-IR),X-ray diffraction(XRD),scanning electron microscope(SEM),nitrogen adsorption-desorption method to analyze thermal stability,crystal phases,surface morphology,specific surface area and pore structures of Al2O3-ZrO2 composite membranes demonstrate that:lake this,the composite sol of different molar ratio is an important factor affecting the viscosity of Al2O3-ZrO2 composite sol,with the increase of r,the viscosity of the composite sol decreases and the cracking degree decreases gradually;At the same heat treatment temperature of 800 ℃,the main crystal phase is t-ZrO2 and Al2O3 sol content in the composite membranes inhibited the crystallization and transparency of ZrO2 grains;When composite sol of r=1,the Al2O3-ZrO2 Composite sol is clear and transparent as well as it’s no cracking after drying,the viscosity was 2.65 mPa·s.The prepared Al2O3-ZrO2 composite membrane had a good thermal stability,compact structure,narrow pore size distribution,the grain size is 31.30 nm.The specific surface area and average pore diameter are 84.98 m2/g and 9.75 nm respectively. 

Funds:
陕西省科技厅重点研发计划专项资金(2017GY-128)

AuthorIntro:
第一作者个人简介:王佳悦(1995-),女,陕西西安人,研究生在读,从事环保新材料的应用研究。电子信箱Email:981084326@qq.com。通讯作者,E-mail:1018915428@qq.com

Reference:
 [1]张慧梅,薛群虎,田晓利,等.凝胶结合Al2O3-ZrO2复相陶瓷性能研究[J].中国陶瓷,2011(2):23-26.
[2]刘志刚.Al2O3-ZrO2陶瓷复合材料的制备和强韧化机理研究[D].青岛:中国海洋大学,2009.
[3]杜红菊.多孔Al2O3-ZrO2陶瓷的微观结构[J].现代技术陶瓷,2015,36(4):50-53.
[4]Gandhi AS,Jayaram V,Chokshi AH.Densification studies on amorphous ZrO2-Al2O3 powder [J].Minerals Metals&Meterials Society,1999.
[5]Gandhi AS, Jayaram V,Chokshi AH.Low temperature densificaton behaviour of metastable phases in ZrO2-Al2O3 powders produced by spray pyrolysis[J].Materials Science&Engineering A,2001,s 304-306(1):785-789.
[6]Gandhi AS, Jayaram V.Pressure consolidation of amorphous ZrO2-Al2O3 by plastic deformation of powder particles[J].Acta Materialia,2002,50(8):2137-2149.
[7]Gandhi AS, Jayaram V.Plastically deforming amorphous ZrO2-Al2O3[J].Acta Materialia, 2003,51(6):1641-1649.
[8]李强伟,华小红.Al2O3/ZrO2复合金属陶瓷模具材料的研究[J].中国陶瓷,2014(11):70-73.
[9]刘国玺,李克智,李国斌.ZrO2添加量对Al2O3-ZrO2复相陶瓷性能的影响[J].兵器材料科学与工程,2015(4):37-40.
[10]李健生,郝艳霞,张烨,等.以无机盐前驱体制备中空纤维担载Al2O3/ZrO2复合膜[J].稀有金属材料与工程,2006,35(9):1449-1452.
[11]同帜,胡敏盾,董旭娟,等.SiO2-ZrO2复合膜的制备及其工艺参数的研究[J].膜科学与技术,2014,34(6):35-38.
[12]周锋,傅迎庆,梁开明,等.工艺参数对TiO2溶胶黏度及胶凝时间的影响[J].大连海事大学学报,2008,34(4):87-90.
[13]吴东兵,刘羽,牛志睿,等.溶胶-凝胶法制备SiO2的溶胶粘度性能研究[J].陕西科技大学学报,2008,26(2):53-56.
[14]郭金玲,沈岳年.用Scherrer公式计算晶粒度应注意的几个问题[J].内蒙古师范大学学报:自然科学版,2009,38(3):357-358.
[15]白周喜,高如琴,周宁生,等.ZrO2含量对Al2O3/ZrO2复相陶瓷微观结构和力学性能的影响[J].硅酸盐通报,2013,32(8):1640-1644.
[16]同帜,霍乐乐,董旭娟,等.溶胶-凝胶法制备氧化锆薄膜的工艺与表征[J].粉末冶金材料科学与工程,2016,21(1):174-179.
[17]同帜,行静,樊璐,等.以硝酸铝为前驱体制备Al2O3薄膜及其表征[J].膜科学与技术,2017,37(5):56-60.

Service:
Download】【Collect

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone:010-80492417/010-80485372; Fax:010-80485372 ; Email:mkxyjs@163.com

京公网安备11011302000819号