膜科学与技术

位置：首页 >> 期刊内容阅读

气隙长度与芯液浓度对纤维素中空纤维膜结构与性能的影响

作者：梁义宋俊程博闻陆飞

单位：天津工业大学中空纤维膜材料与膜过程教育部重点实验室

关键词：气隙长度; 芯液浓度; 氯代1-烯丙基-3-甲基咪唑; 纤维素; 中空纤维膜

DOI号：

分类号： TQ028.8

出版年,卷(期):页码： 2011,31(2):83-88

摘要：

以离子液体氯代1-烯丙基-3-甲基咪唑([AMIM]Cl)为溶剂来纺制纤维素中空纤维膜，考察了气隙长度与芯液浓度对中空纤维膜结构与性能的影响。采用扫描电子显微镜(SEM)对膜内、外表面形态及支撑层结构进行了观察，测试了中空纤维膜的水通量、截留率等渗透性能以及最大拉伸强度、断裂伸长率、杨氏模量等力学性能。结果表明：随着气隙长度与芯液浓度的增加，中空纤维膜外表面与支撑层孔洞结构变小，内表面结构变得更加规整，膜孔隙率与水通量下降，最大拉伸强度、断裂伸长率、杨氏模量等力学性能则逐渐变大；与芯液浓度相比，气隙长度对中空纤维膜性能的影响较为显著。

The cellulose hollow fiber membranes were spinned using ionic liquid 1-ally-3methylimidazolium chloride([AMIM]Cl) as solvent. Influence of air gap length and bore liquid concentration on the hollow fiber membranes structure and properties were investigated. Inner- and outer- surfaces morphology and the support layer structure of the membranes were studied using scanning electron microscopy(SEM). Furthermore, permeation properties and mechanical properties of the membranes, including water flux, retention rate, ultimate tensile strength(UTS), elongation at break, young's modulus were also tested. The results induce that, with the increase of air gap length and bore liquid concentration, the pores become smaller and the inner surface show more regular. Contrary to decreased porosity and water flux, mechanical properties of ultimate tensile strength, elongation at break, young's modulus show a increased tendency. Compared with the bore liquid concentration, the air gap length has a more significant influence on the hollow fiber membrane properties.

基金项目：

作者简介：

第一作者：梁义，（1985- ）男，河南周口人，硕士研究生，主要研究纤维素中空纤维膜，E-mail: liangyi_tjpu@yahoo.cn； *通讯作者：程博闻，（1963- ）男，湖北黄冈人，教授，主要从事膜材料及工艺研发工作，E-mail: bowen@tjpu.edu.cn

参考文献：

[1] E Drioli, L Giorno. Membrane operations: Innovative Separations and Transformations[M]. Germany: WILEY -VCH Verlag GmbH & Co. KGaA,2009.23-25
[2] 杨鹏飞. 纤维素在膜科学中的研究进展[J]. 河北化工，2009,32(4):9-12
[3] E Saljoughi,T Mohammadi.Cellulose acetate(CA)/polyvinylpyrrolidone (PVP)blend asymmetric membran-es:Preparation, morphology and performance[J].Desalination ,2009,249:8 50-854
[4] M R Pekny, A R Greenberg, V Khare, et al.Macrovoid pore formation in dry-cast cellulose acetate membranes: buoyancy studies[J].Journal of Membrane Science,2002,205:11-21
[5] 李红剑,李雄岩,贺晓泉,等. 凝固条件对α-纤维素中空纤维膜结构和性能的影响[J].高分子学报,2007(3):250-254
[6] B Chakrabarty, A K Ghoshal, M K Purkait.Effect of molecular weight of PEG on membrane morphology and transport properties[J].Journal of Membrane Science,2008,309:209-221
[7] S Zhang, C F Fu, F X Li,et al.Direct Preparation of a Novel Membrane from Unsubstituted Cellulose in NaOH Complex Solution[J].Iranian Polymer Journal,2009,18 (10):767-776
[8] T Mohammadi,E Saljoughi.Effect of production conditions on morphology and permeability of asymmetric cellulose acetate membranes[J].Desalination, 2009,243:1-7
[9] 张耀鹏,邵惠丽,沈新元,等. NMMO 法纤维素膜的结构与性能[J].膜科学与技术,2002,22(4):13-25
[10] P Kubisa.Ionic Liquids as Solvents for Polymerization Processes–Progress and Challenges[J]. Progress in Polymer Science,2008,doi:10.1016/j.progpolymsci.2009.09.001
[11] 程博闻，郑伟，臧洪俊. 离子液体法制备纤维素中空纤维膜[P].中国，发明专利，CN101234297A.
2008-8-6
[12] H Zhang, J Wu, J Zhang, et al.1-Allyl-3-methylimidazolium Chloride Room Temperature Ionic Liquid:A New and Powerful Nonderivatizing Solvent for Cellulose[J].Macromolecules ,2005, 38(20):8272-8277
[13] D A Fort,R C Remsing,R P Swatloski,et al.Can ionic liquids dissolve wood? Processing and analysis of lignocellulosic materials with 1-n-butyl-3-methylimidazolium chloride[J].Green Chemistry, 2007, 9:63-69
[14] 吕阳成,吴影新.凝固浴组成对NMMO法纤维素膜形貌的影响[J]. 高等化学工程学报，2007,21(3):398-403
[15] W L Chou, D G Yu, M C Yang.In?uence of Coagulant Temperature and On-Line Drawing on the Mechanical Properties and Permeation Performance of Cellulose Acetate Hollow Fibers[J]. Journal of Polymer Research, 2005,12: 219-229
[16] J H Kim, K H Lee. Effect of PEG additive on membrane formation by phase inversion[J]. Journal of Membra -ne Science,1998,113:853-163
[17] B Chakrabarty, A K Ghoshal, M K Purkait.Effect of molecular weight of PEG on membrane morphology and transport properties[J]. Journal of Membrane Science,2008,309:209-221
[18] E Saljoughi, M Sadrzadeh, T Mohammad.Effect of preparation variables on morphology and pure water permeation ?ux through asymmetric cellulose acetate membranes[J].Journal of Membrane Science,2009, 326:627-634
[19] M Khayet.The effects of air gap length on the internal and external morphology of hollow fiber membranes [J].Chemical Engineering Science,2003,58:3091-3104
[20] S A McKelvey, D T Clausi, W j Koros. A guide to establishing hollow fiber microscopic properties for membrane applications[J].Journal of Membrane Science,1997,124:223-232
[21] T H Young, L W Chen.Pore formation mechanism of membranes from phase inversion process[J]. Desalinati -on,1995,103:233-247

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com