聚偏氟乙烯中空纤维膜的脱氧性能研究

作者：郭培丽，陈华艳，吕晓龙，武春瑞，张庆磊，刘捷

单位：天津工业大学,生物化工研究所，

关键词：脱氧；PVDF；内径；壁厚；长度；表面结构

DOI号：

分类号： TQ028.8

出版年,卷(期):页码： 2012,32(4):6-10

摘要：

采用聚偏氟乙烯（PVDF）中空纤维膜对水中的溶解氧进行了脱氧研究，考察了不同内径、壁厚、长度以及不同表面结构的PVDF中空纤维膜对脱氧效率的影响。结果表明，膜的内径、长度和膜的表面结构对脱氧效率的影响很大，内径越小，组件越长，脱氧效率越好，疏松的海绵状孔结构更利于脱氧。壁厚对中空纤维膜的脱氧效率影响不显著。结合中空纤维膜的力学性能，内凝固浴为N-N二甲基乙酰胺(DMAc)，内径0.3mm，壁厚0.15mm的中空纤维膜更适于脱气。

The degassing performance of polyvinylidene fluoride (PVDF) hollow fiber membrane was studied in this paper with the purpose of improving deoxidizing efficiency. The influence of the inner diameter, wall thickness, module length and the surface morphology on the deoxidizing efficiency has been investigated. The result indicates that the inner diameter, the module length and the surface morphology of the membrane have a great influence on the deoxidizing efficiency. Higher inner diameter and longer module induce higher deoxidizing efficiency. The loose sponge structure of surface of membrane leads to higher deoxidizing efficiency. The effect of the wall thickness of PVDF membrane on the deoxidizing efficiency might be neglected. The hollow fiber membrane with internal coagulant of 70% DMAc, inner diameter of 0.3mm and wall thicknss of 0.15mm would be a better degassing membrane according to the deoxidizing efficiency and mechanics performance of membrane.

基金项目：

天津市重点基金课题（09JCZDJC26300）；天津市科技计划项目（09ZCKFSH02600）

作者简介：

郭培丽（1986-），女，河北石家庄人，硕士生，主要从事脱气膜的研究，guopeili163@163.com。*通讯联系人

参考文献：

[1] 吴津京.脱气膜在给水处理中的研究与应用[D]:[学位论文].北京:北京交通大学,2006. 3-50.
[2] 刘慧峰.膜接触器除氧性能试验研究及其传质分析[D]:[学位论文].上海:上海交通大学,2006. 1-31.
[3] 肖公奎.中空纤维膜接触器脱除水中溶解氧的研究[D]:[学位论文].大连:大连理工大学,2008. 3-33.
[4] Shao Jiahui, Liu Huifeng, He Yiliang. Boiler feed water deoxygenation using hollow fiber membrane contactor [J]. Desalination, 2008,234:370-377.
[5] 吴津京,韩虹林,高杰,等.中空纤维膜脱氧工艺处理给水的试验研究[J]. 能源环境保护,2006,20(6):36-37.
[6] Sengupta A, Peterson P A, Miller B D, et al. Large-scale application of membrane contactors for gas transfer from or to ultrapure water [J]. Separation and Purification Technology, 1998,14:189-200.
[7] 刘贯一.利用聚丙烯中空纤维膜去除水中溶解氧的研究[J]. 河北理工学院学报,2001,23(3):51-55.
[8] 常李静,刘丽英,丁忠伟,等.真空度对膜法溶解氧解吸过程传质性能的影响[J]. 膜科学与技术,2007,27(2):7-10.
[9] Peng Zanguo, Lee S H, Zhou Tong, et al. A study on pilot-scale degassing by polypropylene(PP) Hollow fiber membrane contactors [J]. Desalination, 2008,234:316-322.
[10] Leiknes T O, Semmens M J. Vacuum degassing using microporous hollow ?ber membranes [J]. Separation and Purification Technology, 2000,22-23:287-294.
[11] 王志魁.化工原理[M] .第三版.北京:化学工业出版社,2004.219-225.
[12] 郭媛,沈志松,许泓瑜,等.膜吸收用聚丙烯和聚偏氟乙烯微孔膜的性能评价[J], 膜科学与技术,2007,27(5):41-45.
[13] ]Li J L, Chen B H. Review of CO2 absorption using chemical solvents in hollow fiber membrane contactors [J]. Separation and Purification Technology, 2005,41:109-122.
[14] 卜海军,于莲,陈鸣才,等.指状和海绵状聚偏氟乙烯多孔膜的制备及表征[J]. 高分子材料科学与工程,2006,22(3):243-246.
[15] 武利顺,孙俊芬,王庆瑞.聚偏氟乙烯膜微孔的形成机理[J]. 膜科学与技术,2007,27(5):13-17.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com