PTFE中空纤维膜用于浸没式真空膜蒸馏脱盐的研究

作者：王红杰¹朱海霖¹郭玉海¹吴益尔²金王勇²张华鹏¹陈建勇¹

单位： 1浙江理工大学先进纺织材料与制备技术教育部重点实验室，浙江杭州 310018

关键词：聚四氟乙烯中空纤维膜；浸没式真空膜蒸馏；脱盐

DOI号：

分类号： TB324

出版年,卷(期):页码： 2013,33(5):54-58

摘要：

通过调整挤出头尺寸，制备出不同壁厚的PTFE中空纤维膜。采用浸没式真空膜蒸馏（SVMD），研究了膜丝壁厚、操作条件、NaCl浓度等对产水通量和脱盐率的影响。结果表明，降低膜壁厚度可增加产水通量；提高料液温度和冷侧真空度可明显提高产水通量；曝气亦可提高产水通量，当曝气量超过6m3/h*m2时，产水通量反而下降。连续运行800h的实验表明，水通量随工作时间的延长而减小，200h后趋于稳定，脱盐率可保持在99.6%以上。

The Polytetrafluoroethylene (PTFE) hollow fiber membranes with two wall thicknesses were prepared through changing the parameters of extrusion head in this paper. The effect of wall thickness, operational conditions and NaCl concentration of water solution on the permeate flux and salt rejection were investigated by means of submerged vacuum membrane distillation (SVMD). The experimental results shows that the permeate flux increases with the decrease of wall thickness of PTFE hollow fiber membrane. The permeate flux significantly increases with the increase of fee temperature and vacuum pressure. The permeate flux can be enhanced after air-blowing the outer surface of PTFE hollow fiber membrane, and then drop till air blowing intensity is greater than 6m3/h*m2. The 800 hours test shows that the permeate flux decreases with the extension of working time. After 200 hours, a constant stable water flux is attained with a salt rejection over 99.6%.

基金项目：

国家科技支撑计划（2013BAC01B01）、教育部新世纪优秀人才支撑计划（NCET-10-0980）、浙江省重大科技专项重大社会发展项目（2012C13006-2）、浙江理工大学博士启动基金（1113808-Y）

作者简介：

王红杰（1987-），男，湖北武汉人；主要研究方向：PTFE中空纤维膜在海水淡化中的应用；E-mail：whj0623@126.com 郭玉海，通讯作者，E-mail：gyh@zstu.edu.cn

参考文献：

[1] Safavi M., Mohammadi T. High-salinity water desalination using VMD. [J] Chemical Engineering Journal, 2009, 149: 191–195.
[2] Tang N., Jia Q., Zhang H.J., Li J.J., Cao S. Preparation and morphological characterization of narrow pore size distributed polypropylene hydrophobic membranes for vacuum membrane distillation via thermally induced phase separation. [J] Desalination 2010, 256: 27–36.
[3] Wu B., Tan X.Y., Li K., Teo W.K. Removal of 1,1,1-trichloroethane from water using a polyvinylidene fluoride hollow fiber membrane module: Vacuum membrane distillation operation. [J] Separation and Purification Technology, 2006, 52: 301–309.
[4] Adnan S., Hoang M., Wang H.T., Xie Z.L. Commercial PTFE membranes for membrane distillation application: Effect of microstructure and support material. [J] Desalination, 2012, 284: 297–308.
[5] 张华鹏, 朱海霖, 王峰, 郭玉海. 聚四氟乙烯中空纤维膜的制备. 膜科学与技术, 2013, 33:17-21.
[6] Ariawan A.B. Paste extrusion of polytetrafluoroethylene fine powder resins [D]. Doctoral Thesis, University of British Columbia, 2001.
[7] Gryta M., Tomaszewska M., Grzechulska J., Morawski A.W. Membrane distillation of NaCl solution containing natural organic matter. [J]. Journal of Membrane Science 2001, 181: 279–287.
[8] 武春瑞, 郝福锦, 贾悦, 吕晓龙, 蹇锡高. PVDF中空纤维疏水膜的鼓气吸收法海水提溴性能研究. [J]. 功能材料2009, 9: 1563-1566.
[9] Schofield R.W., Fane A.G., Fell G.J.D. Gas and vapour transport through microporous membranes. I. Knudsen-Poiseuille transition. [J]. Journal of Membrane Science 1990, 53: 159-171.
[10] Mericq J.P., Laborie S., Cabassud C. Vacuum membrane distillation of seawater reverse osmosis brines. [J]. Water Research 2010, 44: 5260-5273.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com