PLA-PEG-PLA嵌段共聚物合成及其共混改性聚乳酸中空纤维膜抗污染性能研究

作者：沈鹏¹，张秋吉²，杨昌玉¹，陈顺权¹，杜如虚¹

单位： 1. 广州中国科学院先进技术研究所水科学研究中心，广州，511458;

关键词：聚乳酸；聚乳酸-聚乙二醇共聚物；亲水性；抗污染性能

DOI号：

分类号： TQ028.8

出版年,卷(期):页码： 2013,33(6):58-63

摘要：

合成制备了不同分子量的PLA-PEG-PLA嵌段共聚物，并应用1H NMR对其进行测试表征。然后将共聚物作为亲水性添加剂，用自行研发的中空纤维膜纺丝机对应制备了不同的PLA共混中空纤维膜。对制成的中空纤维膜进行水通量、残留率、水接触角、抗污染性能等测试以及SEM观察，研究了该添加剂对PLA中空纤维膜各种性能的影响。结果发现，制成的中空纤维膜超滤性能优异，添加PLA-PEG-PLA嵌段共聚物会提高PLA中空纤维膜的抗污染性能，并且共聚物分子量越大，中空纤维膜的亲水性越好，抗污染性能越好。

PLA-PEG-PLA block copolymers with different molecular weight (MW) were synthesized, and characterized by NMR . Then the copolymer was used as hydrophilic addition agent to prepare PLA hollow fiber membrane by blending method. Many properties of material were tested, such as water permeability,residual property, surface water contact angle, relative permeability, BSA rejection .Samples were also analysed by scanning electron microscope. The results showed that PLA-PEG-PLA with larger Mw lead to higher anti-fouling properties in accordance.

基金项目：

作者简介：

沈鹏，男，安徽宿州，硕士研究生，中级工程师二级，国家高级水处理师，主要从事膜分离过程的设计与控制， E-mail:hishenpeng@giat.ac.cn,Tel:15986691661

参考文献：

[1] Sasatsu M, Onishi H, Machida Y. Preparation and biodisposition of methoxypolyethylene glycol amine-poly(DL-lactic acid) copolymer nanoparticles loaded with pyrene-ended poly(DL-lactic acid)[J]. International Journal of Pharmaceutics, 2008, 358(1-2):271-277.
[2] Vink E T H, Rabago K R, Glassner D A, et al. Applications of life cycle assessment to NatureWorksTM polylactide (PLA) production[J]. Polymer Degradation and Stability, 2003, 80(3):403-419.
[3] 曹燕琳,尹静波,颜世峰.生物可降解聚乳酸的改性及其应用研究进展[J]高分子通报, 2006, 10: 90-97.
[4] Imre B, Keledi G, Renner K, et al. Adhesion and micromechanical deformation processes in PLA/CaSO4 composites [J].Carbohydrate Polymers, 2012, 89(3):759-767.
[5] Rouzes C, Leonard M, Durand A, et al. Influence of polymeric surfactants on the properties of drug-loaded PLA nanosphers [J]. Colloids and Surfaces B: Biointerfaces, 2003, 32(2): 125-135.
[6] Frone A N, Berlioz S, Chailan J F, et al. Morphology and thermal properties of PLA-cellulose nanofibers composites [J]. Carbohydrate Polymers, 2013, 91(1-2):377-384.
[7] Zhou H, Lawrence J G, Bhaduri S B. Fabrication aspects of PLA-CaP/PLGA-CaP composites for orthopedic applications: A review [J]. Acta Biomaterialia, 2012, 8(6):1999-2016.
[8] Ho C H, Wang C H, Lin C I, et al. Synthesis and characterization of TPO-PLA copolymer and its behavior as compatibilizer for PLA/TPO blends [J]. Polymer, 2008, 49(18):3902-3910.
[9] 马会茹,官建国,柳娜,等.PEG链段对聚乙二醇接枝聚苯胺结构与性能的影响[J].高分子学报,2006,2(1):92-96.
[10] Lila A S A, Eldin N E, Ichihara N E, et al. Multiple administration of PEG-coated liposomal oxaliplatin enhances its therapeutic efficacy: A possible mechanism and the potential for clinical application [J]. International Journal of Pharmaceutics, 2012, 438(1-2):176-183.
[11] Toral P G, Hervas G, Bichi E, et al. Tannins as feed additives to modulate ruminal biohydrogenation: Effects on animal performance, milk fatty acid composition and ruminal fermentation in dairy ewes fed a diet containing sunflower oil [J]. Animal Feed Science and Technology, 2011, 164(3-4):199-206.
[12] Essa S, Rabanel J M, Hildgen P. Characterization of rhodamine loaded PEG-g-PLA nanoparticles NPs): Effect of poly(ethylene glycol) grafting density [J]. International Journal of Pharmaceutics, 2011, 411(1-2): 178-187.
[13] Ruan G, Feng S S. Preparation and characterization of poly(lactic acid)-poly(ethylene glycol)-poly(lactic acid)(PLA-PEG-PLA) microspheres for controlled release of paclitaxel [J]. Biomaterials, 2003, 24(27):5037-5044.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com