热致相分离法制备聚偏氟乙烯中空纤维微孔膜

作者：安亚欣¹，²，李凭力¹，²?，吴浩赟¹，²，常贺英¹

单位： 1.天津大学化工学院，天津300072；

关键词：热致相分离法；聚偏氟乙烯；中空纤维膜；结构；性能

DOI号：

分类号： TQ028.8

出版年,卷(期):页码： 2013,33(6):13-19

摘要：

本文从聚偏氟乙烯（PVDF）/三乙酸甘油酯（GTA）/癸二酸二丁酯（DBS）体系中，采用热致相分离法，制备聚偏氟乙烯（PVDF）中空纤维微孔膜。研究了铸膜液的组成：混合稀释剂中GTA的含量、PVDF含量，和纺丝条件：空气隙距离、水浴温度、挤出温度，对PVDF中空纤维膜的结构和性能的影响。结果表明：随着混合稀释剂中的GTA质量分数从30%增加至50%，膜的断面由双连续结构转变为变形的球晶与双连续共存的结构。低的PVDF含量、长的空气隙距离、高的水浴温度，均利于膜水通量的提高，但膜对牛血清蛋白的截留率下降，拉伸强度减小。挤出温度升高，膜的水通量先增加后减小，截留率和拉伸先减小后增加。

Poly(vinylidene fluoride) (PVDF) hollow fiber microporous membrane was prepared using mixed diluent of glyceryl triacetate (GTA) and dibutyl sebacate (DBS) via thermally induced phase separation (TIPS). A systematic study was carried out to investigate effects ofthe components of casting membrane solution: GTA content in mixed diluent, PVDF content in the casting membrane solution, and spinning parameters: water bath temperature, air-gap distance, extruding temperatureon the structure and performance of PVDF hollow fiber membrane. It was found that the cross section of membrane changed from interconnected structure into the combination of spherulitic and interconnected structure as GTA mass content in the mixed diluent increased from 30% to 50%. The water flux of PVDF hollow fiber membrane increased as PVDF mass content in the casting membrane solution decreased, the air-gap distance increased, or the water bath temperature increased, however, the solution rejection and the tensile strength of PVDF hollow fiber membrane decreased. As the extruding temperature increased, the water flux of PVDF hollow fiber membrane increased firstly and then decreased, while thesolution rejection and the tensile strength of PVDF hollow fiber membrane decreased firstly and then increased.

基金项目：

作者简介：

安亚欣（1989-），女，河北石家庄人，在读硕士，从事高分子膜的研究。?通讯联系人tdlpl@163.com

参考文献：

[1]Castro A J,Park O. Method for Making MicroporousProducts[P].US:4247498,1981-1-27.
[2]林亚凯, 唐元晖, 马恒宇, 等.热致相分离法制备聚偏氟乙烯微孔膜[J].膜科学与技术,2009,29(6):36-44。
[3]曾一鸣,丁怀宇,施艳荞,等.热致相分离法微孔膜[J].膜科学与技术,2006,26(5):93-98。
[4]GuM H, Zhang J, Wang X L, et al..Formation ofpoly(vinylidene fluoride) (PVDF) membranes viathermally induced phase separation[J].Desalination 2006,192(1-3):160–167.
[5]LloydDR, Kinzer K E, Tseng H S..Microporous membrane formation via thermally induced phase separation. I. Solid-liquid phase separation[J].Journal of Membrane Science,1990,52(3): 239–261.
[6]Cui ZY,DuCH,Xu YY, et al..Preparation of Porous PVdF Membrane via ThermallyInduced Phase Separation Using Sulfolane[J]. Journal of Applied Polymer Science, 2008,108(1):272–280.
[7]Ji G L,Zhu L P,ZhuBK,et al.. Structure Formation and Characterization of PVDF Hollow Fiber Membrane Prepared via TIPS with Diluent Mixture[J].Journal of Membrane Science,2008,319(1-2):264-270.
[8]Rajabzadeh S,Maruyama T,SotaniT,et al..Preparation of PVDF Hollow Fiber Membrane from a Ternary Polymer/Solvent/Nonsolvent System via Thermally Induced Phase Separation (TIPS) Method[J].Separation and Purification Technology,2008,63(2):415-423.
[9]BottinnoA,Camera-Roda G,Capannelli G,et al.. The Formation of Microporous Polyvinylidene Difluoride Membrane by Phase Separation[J].Journal of Membrane Science,1991,57(1):1-20.
[10]Su Y,Chen C X,Li Y G,et al..PVDF Membrane Formation via Thermally Induced Phase Separation[J].Journal of Macromolecular Science,Part A: Pure and Applied Chemistry,2007,44(1):99-104.
[11]MatsuyamaH,Okafuji H,Maki T,et al..Preparation of Polyethylene Hollow Fiber Membrane via Thermally Induced Phase Separation[J].Journal of Membrane Science,2003,223(1-2):119-126.
[12]杨振生.热致相分离法iPP中空纤维微孔膜及其形态结构研究[D].天津大学,2005。
[13]Wu Q Y,Wan L S,Xu Z K,et al..Structure and Performance of Polyacrylonitrile Membrane Prepared via Thermally Induced Phase Separation[J].Journal of Membrane Science,2012,409-410:355-364.
[14]Qiu Y R,Matsuyama H.Preparation and Characterization of Poly(vinyl butyral) Hollow Fiber Membrane via Thermally Induced Phase Separation with Diluent Polyethylene Glycol 200[J].Desalination,2010,257(1-3):117-123.
[15]BrandrupJ,ImmergutE H,Grulke E A. Polymer Handbook[M].New York: Wiley,1999.
[16]HansenC M. Hansen Solubility Parameters: A User’s Handbook[M].Boca Raton: CRC,2007.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com