聚醚共聚酰胺-三醋酸甘油酯多层复合气体分离膜的制备及其分离性能 |
作者:王颖1,2,任吉中1, ,徐徜徉3,李晖1,冯世超1,邓麦村1 |
单位: 1. 洁净能源国家实验室,大连化学物理研究所,大连116023; 2. 中国科学院大学,北京 100049;3. 膜技术国家工程研究中心,大连116023 |
关键词: 聚醚共聚酰胺;三醋酸甘油酯;二氧化碳分离 |
出版年,卷(期):页码: 2014,34(5):27-32 |
摘要: |
本文以聚醚共聚酰胺Pebax1074为分离层主体膜材料,以三醋酸甘油酯(GTA)为添加剂,制备具有超薄分离层的Psf/PDMS/Pebax1074和Psf/PDMS/Pebax1074-GTA/PDMS多层复合气体分离膜.考察了Pebax1074和GTA浓度、温度、压力等条件对H2、 N2、CH4和CO2等在复合膜中的渗透性能的影响.结果显示,随Pebax1074浓度的增大,Psf/PDMS/Pebax1074膜对气体的渗透通量急剧下降,气体选择性逐渐增大至接近Pebax1074本征值.当GTA含量大于50wt%, Psf/PDMS/Pebax1074-GTA复合膜的气体渗透通量大幅增加,而气体选择性不高.利用硅橡胶对复合膜表面保护后,气体选择性接近Pebax1074材料本征值. Psf/PDMS/Pebax1074-GTA/PDMS多层复合膜对CO2具有较高的渗透通量和较高的选择性.CO2对多层复合膜存在塑化效应,渗透通量随压差增大而增大;随着操作温度的升高,H2、N2、CH4和CO2在复合膜中的渗透通量显著增大,而CO2/(N2、CH4、H2)的分离系数减小. |
This paper describes the performance of Pebax1074/glycerol triacetate (GTA) blend composite membranes for CO2 separation. First the influence of mass content of Pebax1074 and GTA on the performance of composite membranes is investigated. The gas permeance decreases as the content of Pebax1074 increases for Psf/PDMS/Pebax1074 composite membranes. And for Psf/PDMS/Pebax1074-GTA composite membranes, when the GTA content exceeds 50wt%, the gas permeance increases greatly, but the gas selectivity is not high. In order to increase the membrane selectivity, the PDMS sealing layer is used and different operating conditions are observed. The Psf/PDMS/Pebax1074-GTA/PDMS composite membrane has high flux and selectivity for CO2 separation. Due to plasticization effect, the CO2 permeance increases with the increase of transmembrane pressure. The permeance of different gases increases as temperature increases, and the selectivities of CO2/(N2、CH4、H2) decrease. |
王颖(1990-),女,河南灵宝人,硕士,从事膜分离过程研究.?通讯联系人,renjizhong@dicp.ac.cn |
参考文献: |
[1] Rubin E S, Mantripragada H, Marks A, et al. The outlook for improved carbon capture technology[J]. Prog Energ combust Sci, 2012,38(5): 630-671. [2] Rao A B, Rubin E S. A technical, economic, and environmental assessment of amine-based CO2 capture technology for power plant greenhouse gas control[J]. Environ Sci Technol , 2002,36(20): 4467-4475. [3] Gomes D, Peinemann K V, Nunes S P, et al. Gas transport properties of segmented poly(ether siloxane urethane urea) membranes[J]. J Membr Sci, 2006,281(1-2): 747-753. [4] Liu L, Chakma A, Feng X S. Propylene separation from nitrogen by poly(ether block amide) composite membranes[J]. J Membr Sci, 2006,279(1-2):645-654. [5] Ren Xiaoling, Ren Jizhong, Li Hui,et al. Poly (amide-6-b-ethylene oxide) multilayer composite membrane for carbon dioxide separation[J]. Int J Greenh Gas Con, 2012,8:111-120. [6] Liu L, Chakma A, Feng X S. A novel method of preparing ultrathin poly(ether block amide) membranes[J]. J Membr Sci, 2004,235(1-2):43-52. [7] 冯世超,任吉中,任晓灵,等. 聚醚共聚酰胺/聚乙二醇共混膜的制备及其气体渗透性能的研究[J].膜科学与技术,2012,05:27-33. [8] Car A, Stropnik C, Yave W, et al. PEG modified poly(amide-b-ethylene oxide) membranes for CO2 separation [J]. J Membr Sci, 2008,307(1): 88-95. [9] Liu L, Chakma A, Feng X S. CO2/N2 separation by poly(ether block amide) thin film hollow fiber composite membranes[J]. Ind Eng Chem Res,2005,44(17):6874-6882. [10] Car A, Stropnik C, Yave W, et al. Pebax (R)/polyethylene glycol blend thin film composite membranes for CO2 separation: Performance with mixed gases[J]. Sep Purif Technol, 2008,62(1):110-117. [11] Murali R S, Sridhar S, Sankarshana T, et al. Gas Permeation Behavior of Pebax-1657 Nanocomposite Membrane Incorporated with Multiwalled Carbon Nanotubes.[J].Ind Eng Chem Res, 2010,49(14): p. 6530-6538. [12] Liu L, Chakma A, Feng X S. Preparation of hollow fiber poly(ether block amide)/polysulfone composite membranes for separation of carbon dioxide from nitrogen[J]. Chem Eng J, 2004,105(1-2):43-51. [13] Pichard S. A gas permeable membrane[P]. WO2008/017307 A1.2008. [14] Yave W, Car A. Peinemann K V,et al. Gas permeability and free volume in poly(amide-b-ethylene oxide)/polyethylene glycol blend membranes[J]. J Membr Sci, 2009,339(1-2):177-183. [15] Miller M B. Highly CO2-Philic Liquid Oligomers and Phase Change-Solvents for the Absorption of CO2.[D].2011, University of Pittsburgh. [16] Feng Shichao, Ren Jizhong, Li Zhansheng, et al. Poly (amide-12-b-ethylene oxide)/glycerol triacetate blend membranes for CO2 separation[J]. Int J Greenh Gas Con, 2013,19(0):41-48. [17] Ribeiro C P, Freeman B D. Carbon dioxide/ethane mixed-gas sorption and dilation in a cross-linked poly(ethylene oxide) copolymer[J]. Polymer, 2010,51(5):1156-1168. [18] Lin H, Freeman B D. Gas solubility, diffusivity and permeability in poly(ethylene oxide)[J]. J Membr Sci, 2004,239(1):105-117. |
服务与反馈: |
【文章下载】【加入收藏】 |
《膜科学与技术》编辑部 地址:北京市朝阳区北三环东路19号蓝星大厦 邮政编码:100029 电话:010-64426130/64433466 传真:010-80485372邮箱:mkxyjs@163.com
京公网安备11011302000819号