| 聚丙烯腈/聚氨酯共混相容性对共混膜性能的影响 |
| 作者：王海博1，邱广明2 |
| 单位： 1内蒙古工业大学 土木工程学院，2内蒙古工业大学 能源与动力工程学院，呼和浩特 010051 |
| 关键词： 聚丙烯腈；聚氨酯；共混；微孔膜；相容性 |
| DOI号： |
| 分类号： TB324；TB332 |
| 出版年,卷(期):页码： 2015,35(6):67-71 |
|
摘要： |
|
以聚丙烯腈和聚氨酯为膜材料，N，N-二甲基乙酰胺为溶剂，采用相转化法制备微孔膜。研究了聚合物相容性对共混膜的结构和性能的影响。结果表明:PAN/PU为部分相容体系；当聚合物的比例为8/2，质量分数为16%时，膜水通量为773.2L/（m2h），对牛血清蛋白的截留率为87.7%，此时膜性能最佳；共混比在7/3到9/1之间，膜的力学性能较好。 |
|
The blended microporous membrane of polyacrylonitrile and polyurethane was prepared by phase inversion method with N, N-dimethylacetamide as solvent. The influences of polymer compatibility on membrane structure and performance were studied. The results show that PAN/PU is partially compatible system；with blending ratio of 8:2 and the polymer mass fraction of 16%, the performance of the blended membrane is the best: The water flux is 773.2L/（m2h）and the retention rate is 87.7%.When blending ratio is in between 7:3 and 9:1, the membrane has good mechanical properties. |
|
基金项目： |
| 国家自然科学基金项目（51263013）；内蒙古自然科学基金（2011MS0802） |
|
作者简介： |
| 王海博（1987-），女，陕西西安，主要研究方向：膜分离和水处理技术，E-mail：327947362@qq.com |
|
参考文献： |
| [1] A.Cassano，A.Basile.20-Membranes for industrial microfiltration and ultrafiltration[M].Advanced Membrane Science and Technology for Sustainable Energy and Environmental Applications,2011：647-679 [2] 赟丽赋,赵强,钱锦文.共聚改性聚丙烯腈微孔膜制备和分离性能的研究[J].高校化学工程学报,2007(4)：211-215 [3] Telma Barroso,Márcio Temtem,Teresa Casimiro,Ana Aguiar-Ricardo.Antifouling performance of poly(acrylonitrile)-based membranes:From green synthesis to application[J].The Journal of Supercritical Fluids,2011,(3):312-321 [4] S.Gopakumar,M.R.Gopinathan Nair.Determination of molecular parameters of NR/PU block copolymers by transport studies[J].European Polymer Journal,2005,(9):2002-2009 [5] 许昆鹏，王如.聚氨酯在分离膜中的应用研究进展[J].塑料制造，2008,(2):1-3 [6] H.Kumara,Siddaramaiahb.Chemical compatibility of PU/PAN interpenetrating polymer network membrane with substituted aromatic solvents[J].Journal of Hazardous Materials,2007,(1-2):467-476 [7] 安树林，石波.聚丙烯腈/聚氨酯熔纺一拉伸致孔分离膜共混结构的研究[J].天津工业大学学报,2004,(8):28-31 [8] 赵素合主编.聚合物加工工程[M].北京.中国轻工业出版社,2001,3:16-21 [9] 游长江，石小华.溶解度参数分析PVC共混物相容性[J].化学建材,1999（4):9-12 [10] 杨彦功，贾曌.腈纶表面接枝大豆蛋白的初步实验[J].纺织学报,2006,27（6）:62-63 [11] P.A.A.P.MAMZA，F.M .FOLARANMI.Compatibility studies on solution of poly styrene and polyvinyl acetate blend by density and viscometric methods[J].Eur.Polym,1996,32（7):909-912 [12] 方少明，王明花.聚丙烯腈共混超滤膜的研究[J].郑州轻工业学院学报,2005,(1):28-30 [13] 马建华.共混改性丙烯的研究[J].合成纤维,1999,28(4):12-17 [14] 徐又一，徐志康.高分子膜材料[M].北京.化学工业出版社,2005:44-45 |
|
服务与反馈： |
| 【文章下载】【加入收藏】 |
《膜科学与技术》编辑部 地址：北京市朝阳区北三环东路19号蓝星大厦 邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com
京公网安备11011302000819号