ZrO2溶胶的稳定性及溶胶-凝胶材料转变的物相-化学结构分析

作者：杨靖，李淋钰，李波，郭英明，马嘉莹

单位：西安工程大学城市规划与市政工程学院

关键词：溶胶-凝胶过程；ZrO2溶胶；凝胶材料；溶胶稳定性；粘滞性活化吉布斯自由能

DOI号：

分类号： O484

出版年,卷(期):页码： 2018,38(4):23-26

摘要：

以Zr(NO3)4·5H2O为前驱体，采用溶胶-凝胶法制备ZrO2溶胶.通过测定ZrO2溶胶的密度、粘度，计算ZrO2溶胶体系的粘滞性活化吉布斯自由能，采用红外光光谱、粒径分析、X射线衍射（XRD）和扫描电镜（SEM）对ZrO2溶胶及其凝胶材料进行分析表征。结果表明，所形成的ZrO2溶胶粒径小且分布窄，平均粒径为2.89 nm。在25℃陈化的前60d内，ZrO2溶胶的密度、粘度、粒径以及粘滞性活化吉布斯自由能略有增大，表明溶胶体系内部颗粒间有较大的摩擦力，溶胶稳定性和分散性良好。ZrO2溶胶及其凝胶材料中均没有Zr-O键，Zr元素是以无定型ZrOC2O4·2H2O的形式存在，400℃焙烧后出现的是四方相ZrO2晶体。

ZrO2 sol was prepared by sol-gel method using Zr(NO3)4·5H2O as precursor. The Gibbs free energy of ZrO2 sol system was calculated by measuring the density and viscosity of ZrO2 sol. Infrared spectra (IR), particle size analysis, X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the properties of ZrO2 sol and its gel material. The results show that the freshly prepared ZrO2 sol has a narrow particle size distribution with an average particle size of 2.89 nm. Within the first 60 days aged at 25℃, the density, viscosity, particle size and viscosity-activated Gibbs free energy of ZrO2 sol slightly increase, indicating that the great friction exists among the particles of the system and ZrO2 sol has good stability and dispersibility. There is no Zr-O bond in the ZrO2 sol and its gel material, and Zr element exists in the form of amorphous ZrOC2O4·2H2O. Tetragonal ZrO2 crystal appears in the sample calcined at 400℃.

基金项目：

国家自然科学基金(21573171)和陕西省重点研发计划(2017GY-121)

作者简介：

通讯联系人：杨靖（1976- ），女，湖北省武汉市人，博士，西安工程大学教授，主要从事膜材料的制备及分离技术的研究. E-mail: jingy76@163.com

参考文献：

[] 曹义鸣, 徐恒泳, 王金渠. 我国无机陶瓷膜发展现状及展望[J]. 膜科学与技术, 2013, 33(02): 1-5+11.
[] Tahmasebpour M, Babaluo A A, Aghjeh M K. Synthesis of zirconia nanopowders from various zirconium salts via polyacrylamide gel method[J]. Journal of the European Creamic Society, 2008, 28(4):773-778.
[] 宋大雷, 刘思奇, 李丰, 等. 硅烷改性纳米ZrO2对镁锂合金表面环氧树脂涂层耐蚀性能的影响[J]. 高等学校化学学报, 2017, 38(01):77-84.
[] 郭攀, 常弈, 王毅, 等. 模板剂对合成氧化锆晶体性质的影响研究[J]. 人工晶体学报, 2014,43(10): 2687-2692.
[] 李慧. 负载型ZrO2催化剂的制备、表征及氨氧化反应性能研究[D]. 吉林大学, 2017.
[] 高悝, 叶春, 李春华. 纳米材料用于改性水处理中的有机-无机杂化膜的研究进展[J]. 应用化工, 2017, 46(10):1999-2004.
[] 同帜, 霍乐乐, 董旭娟, 等. 溶胶-凝胶法制备氧化锆薄膜的工艺与表征[J]. 粉末冶金材料科学与工程, 2016, 21(01)：174-179.
[] Nagaprabha P, Bhattacharya S. Rheological characterisation of sol–gel phenomenon and stability of green gram and foxtail millet flour gels[J]. LWT - Food Science and Technology, 2016, 65:917-923.
[] LI L, QI H. Gas separation using sol–gel derived microporous zirconia membranes with high hydrothermal stability[J]. Chinese Journal of Chemical Engineering, 2015, 23(08): 1300-1306.
[]Soo M T, Prastomo N , Matduda A , et al. Elaboration and characterization of sol-gel derived ZrO2 thin films treated with hot water[J]. Applied Surface Science, 2012, 258(13):5250-5258.
[] Hassein-Bey-Larouci A, Igoujilen O, Aitkaci A, et al. Dynamic and kinematic viscosities, excess volumes and excess Gibbs energies of activation for viscous flow in the ternary mixture {1-propanol+N,N-dimethylformamide+chloroform at temperatures between 293.15K and 323.15K[J]. Thermochimica Acta, 2014, 589(10):90-99.
[] LI D, FANG W J, LIU L, et al. Volumetric and viscous properties for binary mixtures of N-methylpiperazine with ethyl acetate or butyl acetate from 298. 15K to 313. 15 K [J]. Chemical Journal of Chinese Universities, 2013, 34(8):1924-1928.
[] Xu Q, Sun S, Lan G, et al. Excess properties and spectral investigation for the binary system diethylene glycol dimethyl ether+water at T=(293.15, 298.15, 303.15, 308.15 and 313.15) K [J]. Chem Eng Data, 2015,60 (1):2-10.
[] 杨凤军, 郭永胜, 魏会, 等. 正构烷烃/JP-10二元体系的体积性质[J]. 高等学校化学学报, 2010, 31(06):1222-1226.
[] 王大志, 罗毅, 杨兰, 等. 非晶氧化锆水合物红外研究[J]. 化学物理学报, 2000, 13(04): 481-486.
[] 刘宇尘, 陈卫平, 聂东红, 等. 铈稳定钪掺杂氧化锆的水热合成与结构表征[J]. 粉末冶金材料科学与工程, 2014, 19(05):715-720.
[] 刘婷婷. 片式氧传感器纳米氧化锆材料的制备及性能研究[D]. 湖南大学, 2015.
[19] 奚红霞, 黄仲涛. 氧化锆前驱体草酸氧锆的制备和表征[J]. 无机材料学报, 1996, 11(03): 547-551.
[20] 王晶,许吉泰,龚念. 水热法制备球形二氧化锆粉体的研究[J]. 硅酸盐通报, 2013,32(05): 936-940.
[21] 李枝芝. 高分散纳米晶ZrO2的一步合成工艺研究[D]. 云南大学, 2016.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com