磺化多巴胺-聚乙烯亚胺共沉积制备聚砜基复合纳滤膜的研究

作者：侯斌，赵晨辉，张健，苏婉，张文娟，程方，常高峰，张宇峰

单位： 1.天津城建大学水质科学与技术天津市重点实验室，天津300384； 2. 天津工业大学省部共建分离膜与膜过程国家重点实验室，天津300387； 3. 天津市生态环境科学研究院，天津300191

关键词：纳滤；磺化多巴胺；聚乙烯亚胺；共沉积

DOI号：

分类号： TQ051.893

出版年,卷(期):页码： 2022,42(3):91-96

摘要：

先将聚多巴胺（PDA）磺化，再将磺化多巴胺（SDA）与聚乙烯亚胺（PEI）一起溶解于Tris缓冲液中，最后在聚砜（PSf）基膜上进行共沉积获得SDA-PEI/PSf复合纳滤膜。通过傅利叶红外光谱、X光电子能谱XPS、扫描电镜、原子力显微镜、膜表面Zeta电位、水接触角、水脱盐等表征膜结构与性能。结果表明，其对硫酸镁的脱盐率随着沉积时间延长和SDA的浓度增加而增加；SDA-PEI的共沉积层均匀附着在膜表面，膜表面电负性亦随SDA增加而增强。

Firstly, polydopamine (PDA) was sulfonated, then sulfonated dopamine (SDA) and polyethylene imine (PEI) were dissolved in Tris buffer, and finally, SDA-PEI/PSf composite nanofiltration membranes were obtained by co-deposition on the polysulfone (PSf) substrate membrane. The structure and properties of the membrane were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy, zeta potential on the membrane surface, water contact Angle, and water desalination. The results show that the desalting rate of magnesium sulfate increases with the increase of deposition time and SDA concentration. The co-deposition layer of SDA-PEI was uniformly attached to the membrane surface, and the electronegativity of the membrane surface increased with the increase of SDA.

基金项目：

国家科技重大专项课题（2017ZX07107-001-003）；国家重点研发计划（2017YFE0114200）；天津市科技重大专项与工程计划（17ZXSTSF00040）

作者简介：

侯斌（1996-），男，山西吕梁人，从事膜改性与水处理技术的方向研究

参考文献：

[1]程毅丽，康国栋，贾静璇，等. 聚四氟乙烯中空纤维膜的多巴胺自聚表面改性及性能研究[J]. 高校化学工程学报,2015, 29(05): 1259-1264.
[2]冯霞，夏伟伟，马潇，等. 多巴胺仿生修饰PVDF微滤膜的制备及性能[J]. 天津工业大学学报, 2018, 37(04): 14-19.
[3]周蓉,任鹏飞,徐志康. 预处理对聚多巴胺改性聚丙烯微滤膜性能影响研究[J]. 膜科学与技术, 2015, (01): 56-63.
[4]Wang L , Wang D , Dong Z , et al. Interface Chemistry Engineering for Stable Cycling of Reduced GO/SnO2 Nanocomposites for Lithium Ion Battery[J]. Nano Letters, 2013.（页码）
[5]Yang H C , Liao K J, Huang H , et al. Mussel-inspired modification of a polymer membrane for ultra-high water permeability and oil-in-water emulsion separation[J]. Journal of Materials Chemistry A, 2014, 2(26):10225-10230.
[6]Wang T, Qiblawey H, Sivaniah E, et al. Novel methodology for facile fabrication of nanofiltration membranes based on nucleophilic nature of polydopamine[J]. Journal of Membrane Science, 2016, 511: 65-75.
[7]Ding J, Wu H, Wu P. Development of nanofiltration membranes using mussel-inspired sulfonated dopamine for interfacial polymerization [J]. Journal of Membrane Science, 2019, 598:117658.
[8]Hamidreza (Jafar) Rezania, Vatanpour V, Shockravi A, et al. Study of synergetic effect and comparison of novel sulfonated and carboxylated bulky diamine-diol and piperazine in preparation of negative charge NF membrane[J]. Separation and Purification Technology, 2019:284-296.
[9]苏婉,张文娟,张宇峰.PDA与PEI共沉积和分步沉积方法对纳滤膜性能的影响[J].膜科学与技术, 2020, 40(03):14-21.
[10]Rezania J, Vatanpour V, Hayatipour M, et al. Synthesis of a novel sulfonated poly(amide-imide) and its application in preparation of ultrafiltration PES membranes as a modifier: ARTICLE[J]. Journal of Applied Polymer Science, 2018:46477.
[11]Chew N, Zhao S, Malde C, et al. Superoleophobic surface modification for robust membrane distillation performance [J]. Journal of Membrane Science, 2017, 541:162-173.
[12]Lv Y, Du Y, Chen Z X, et al. Nanocomposite Membranes of Polydopamine/Electropositive Nanoparticles/ Polyethyleneimine for Nanofiltration [J]. Journal of Membrane Science, 2017:99-106.
[13]Ruan H, Zheng Z, Pan J, et al. Mussel-inspired sulfonated polydopamine coating on anion exchange membrane for improving permselectivity and anti-fouling property [J]. Journal of Membrane Science, 2018: 550:427-435.
[14]Jiang J, Zhu L, Zhu L, et al. Surface Characteristics of a Self-polymerized Dopamine Coating Deposited on Hydrophobic Polymer Films. [J]. Langmuir, 2011, 27(23): 14180-14187.
[15]Dreyer DR, Miller DJ, Freeman BD, et al. Elucidating the Structure of Poly(dopamine)[J]. Langmuir the Acs Journal of Surfaces & Colloids, 2012, 28(15): 6428.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com