作者：任家硕，秦振平，王乃鑫，刘通，倪红旭，安全福

单位：北京工业大学环境与生命学部，北京 100124

关键词： U型中空纤维复合膜；PEBA；渗透汽化；优先透醇

DOI号：

分类号： TQ028.8

出版年,卷(期):页码： 2022,42(4):1-8

摘要：

以聚偏氟乙烯（PVDF）中空纤维超滤膜为基膜，构建了具有U型结构的中空纤维膜组件。采用浸渍-提拉法将聚醚酰胺嵌段共聚物（PEBA）组装到PVDF膜表面，获得了具有优先透醇性能的PEBA/PVDF中空纤维渗透汽化复合膜。分析和表征了组装前后PVDF膜表面的形貌和化学性质，研究了PEBA质量分数、干燥温度、干燥时间和提拉速率等制备条件对复合膜性能的影响，考察了进料温度和进料流速等操作条件的影响。此外，考察了具有U型结构的PEBA/PVDF中空纤维渗透汽化复合膜的稳定性以及对ABE发酵液模拟体系的分离性能。结果表明，PEBA/PVDF中空纤维复合膜在分离1 %（质量分数）正丁醇/水体系时，渗透通量为2720 g/（m2·h)，分离因子为17.38，表现出良好的优先透醇渗透汽化性能。

Polyvinylidene fluoride (PVDF) hollow fiber ultrafiltration membrane was used to construct a hollow fiber membrane module with U-shape structure. The polyether amide block copolymer (PEBA) was assembled on the surface of PVDF membrane by dip-coating and lifting method. The PEBA/PVDF hollow fiber composite membrane was obtained with alcohol permselectivity. The morphology and chemical properties of PVDF membrane before and after assembly were analyzed and characterized. The effects of preparation conditions such as PEBA concentration, drying temperature, drying time and lifting speed on the separation performance of composite membrane were studied. The effects of operating conditions such as feed temperature and feed flow rate on the membrane were also investigated. In addition, the stability of PEBA/PVDF hollow fiber pervaporation composite membrane module with U-shaped structure and the separation performance of ABE fermentation broth simulation system were investigated. The results showed that PEBA/PVDF hollow fiber composite membrane had a permeation flux of 2720 g /（m2·h） and a separation factor of 17.38 in the separation of 1 % （mass fraction）n-butanol/water system, showing a good pervaporation performance.

基金项目：

国家自然科学基金项目（21776003）

作者简介：

任家硕（1996-），男，山东济南人，硕士生，主要从事渗透汽化膜的制备研究

参考文献：

[1]Durre P, Richard T. Fermentative production of butanol—The academic perspective[J]. Current Opinion in Biotechnology, 2011, 22: 331–336.
[2]Verónica G, Johanna P, Heikki O, et al. Challenges in biobutanol production: How to improve the efficiency?[J] Renewable and Sustainable Energy Reviews, 2011, 15: 964–980.
[3]Ni Y, Sun Z H. Recent progress on industrial fermentative production of acetone–butanol–ethanol by Clostridium acetobutylicum in China[J]. Appl Microbiol Biotechnol, 2009, 83: 415–423.
[4]Nidlsen D R, Prather K J. In situ product recovery of n-butanol using polymeric resins[J]. Biotechnology and Bioengineering, 2009, 102: 811-821.
[5]Qureshi N, Blaschek H P. Recovery of butanol from fermentation broth by gas stripping[J]. Renewable Energy, 2001, 22: 557–564.
[6]Li W H, Li J, Wang N X, et al. Recovery of bio-butanol from aqueous solution with ZIF-8 modified graphene oxide composite membrane[J]. Journal of Membrane Science, 2020, 598: 117671.
[7]李育泽, 史宝利. 正庚烷为溶剂高温下制备聚二甲基硅氧烷渗透汽化膜的研究[J]. 膜科学与技术, 2017, 37(1): 81-86.
[8]Cheng X Q, Konstas K, Doherty C M, et al. Organic microporous nanofillers with unique alcohol affinity for superior ethanol recovery toward sustainable biofuels[J]. ChemSusChem, 2017,10: 1887–1891.
[9]王敏敏, 张新儒, 丁川, 等. PEBA/MCM-41杂化膜的制备及其对苯酚/水渗透汽化分离性能的研究[J]. 膜科学与技术, 2015, 35: 40-47.
[10]Liu F F, Liu L, Feng X S, et al. Separation of acetone-butanol-ethanol (ABE) from dilute aqueous solutions by pervaporation[J]. Separation and Purification Technology, 2005, 42: 273-282.
[11]Liu S N, Liu G P, Jin W Q, et al. Hydrophobic-ZIF-71 filled PEBA mixed matrix membranes for recovery of biobutanol via pervaporation[J]. Journal of Membrane Science, 2013, 446: 181-188.
[12]Li Y K, Shen J, Jin W Q, et al. PEBA/ceramic hollow fiber composite membrane for high-efficiency recovery of bio-butanol via pervaporation[J]. Journal of Membrane Science, 2016, 510: 338-347.
[13]Wu G R, Li Y L, Jia Z Q, et al. In situ preparation of COF-LZU1 in poly(ether-block-amide) membranes for efficient pervaporation of n-butanol/water mixture[J]. Journal of Membrane Science, 2019, 581: 1-8.
[14]Bruijn F T, Sun L, Kapteijn F, et al. Influence of the support layer on the flux limitation in pervaporation[J]. Journal of Membrane Science, 2003, 223: 141-156.
[15]Wickramasinghe S R, Semmens M J, Cussler E L. Better hollow fiber contactors[J]. Journal of Membrane Science, 1991, 62: 371-388.
[16]Wang K L, Cussler E L. Baffled membrane modules made with hollow fiber fabric[J]. Journal of Membrane Science, 1993, 85: 265-278.
[17]Liu L Y, Li L J, Ding Z W, et al. Mass transfer enhancement in coiled hollow fiber membrane modules[J]. Journal of Membrane Science, 2005, 264: 113-121.
[18]Yang X, Wang R, Fanel A G, et al. Membrane module design and dynamic shear-induced techniques to enhance liquid separation by hollow fiber modules: A review[J]. Desalination and Water Treatment, 2013, 51: 16-18.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com