PVDF中空纤维膜纺丝配方对膜性能影响的探究

作者：王献德，刘斌，赵晓丹，冯暨伟，张博丰，孙绿合

单位：华电水务装备（天津）有限公司,天津,301700

关键词：中空纤维膜纺丝配方强度通量

DOI号：

分类号： TQ051.893

出版年,卷(期):页码： 2022,42(4):89-95

摘要：

为优化聚偏氟乙烯（PVDF）中空纤维膜的纺丝配方，提高膜的性能，本文采用正交试验设计，通过PVDF质量分数、PVP质量分数、PEG分子量三个因素，研究干湿相转化法制备PVDF中空纤维膜过程中配方对膜性能结构的影响。通过试验测试，可得到以下结论: 铸膜液中PVDF质量分数越多，中空纤维膜的强度、拉伸伸长率都越大，PVDF质量分数是最显著的影响因素；PVP质量分数越多，膜丝通量越高； PVDF质量分数越高，膜丝的孔径越小；通过SEM图对膜丝的形态结构分析， PVDF质量分数增高，膜结构趋于致密，膜外表面孔减少；随着PVP的增多，膜外表面孔增多。综合考虑各个性能参数之间的要求，考虑配方的设计，因素的主次顺序是PVDF质量分数、PVP质量分数、PEG分子量，优选方案可以是PVDF质量分数14%、PVP质量分数20%、PEG分子为600。

In order to optimize the spinning formula of PVDF hollow fiber membrane and improve the performance of PVDF membrane, the effects of the formula on the performance and structure of PVDF hollow fiber membrane prepared by Non solvent induced phase separation method were discussed by using orthogonal experimental design and three factors: PVDF mass fraction, PVP mass fraction and PEG molecular weight. The results showed that the higher the mass fraction of PVDF in the casting solution, the greater the strength and tensile elongation of the hollow fiber membrane. Through the morphological structure analysis of the membrane fibers, the higher the mass fraction of PVDF, the denser membrane fibers structure, the fewer pores of surface face of the membrane fibers, and the smaller pores diameter of the membrane fibers; The higher the mass fraction of PVP, the higher the flux of membrane fibers and the more pores on the outer surface of membrane fibers. Considering the requirements of various performance parameters and the design of formula, the primary and secondary order of factors is PVDF mass fraction, PVP mass fraction and PEG molecular weight. The optimal scheme can be PVDF mass fraction 14%, PVP mass fraction 20% and PEG molecular weight 600.

基金项目：

作者简介：

王献德（1982—），男，广西平南县人，工程师，硕士，长期从事膜技术开发与应用相关工作

参考文献：

[1 ]Saeid Rajabzadeha, Shinya Yoshimotoa, Masaaki Teramotoa，el.CO2 absorption by using PVDF hollow fiber membrane contactors with various membrane structures[J].Separation&Purification Technology, 2009, 69(2):210-220.
[2]KANG G-D, CAO Y-M. Application and modification of polyvinylidene fluoride (PVDF) membranes–A review [J]. Journal of Membrane Science, 2014, 463(1): 145-165.
[3]LIU F, HASHIM N A, LIU Y et. al. Progress in the production and modification of PVDF membranes [J]. Journal of Membrane Science, 2011, 375(1): 1-27.
2017(10):7-12.
[4]RAJABZADEH S, LIANG C, OHMUKAI Y et. al. Effect of additives on the morphology and properties of poly (vinylidene fluoride) blend hollow fiber membrane prepared by the thermally induced phase separation method [J]. Journal of membrane science, 2012, 423(1): 189-194.
[5] Gen-Lung Ji, Li-Ping Zhu, Bao-Ku Zhu, et al. Stricture formation and characterization of PVDF hollow fiber membrane prepared via TIPS with diluent mixture[J].Journal ofMembrane Science; 319(1-2):264-270.
[6]Feng L X，Gang W Y，Long L X，et aL. Morphology changes of polyvinylidene fluoride membrane under different phase separation mechanisms[J]. J Membr Sci，2008，320:477-482.
[7]Chang J，Guo J，Zhang L L，et al.Using green solvent，triethyl phosphate(TEP)，to fabricate highly porous PVDF hollow fiber membranes for membrane distillation [J].Journal of Membrane Science，2017，539:295-304.
[8]S.Y. Zhang. Experiment Design Methods Used in Quality Management. Beijing Institute of Technology Press, Beijing, 1991. (In Chinese).
[9]吕晓龙。中空纤维多孔膜性能评价方法探讨[J].膜科学与技术，2019，39（3）：22-28.
[10] 中华人民共和国国家质量监督检验检疫总局，中国国家标准化管理委员会，GB/T 32361-2015，分离膜孔径测试方法泡点和平均流量法[S],2015：4-6
[11]孙倩云，周玥，汪朝晖，汪效祖，刘飞，崔朝亮。高分离精度抗污染PVDF中空纤维膜的制备。[J].膜科学与技术，2011，31（2）：1-6.Ⅱ
[12]李云雁，胡传荣。试验设计与数据处理[M]。北京：化学工业出版社，2007.83-87.
[13]Reuvers A J, Smolders C A. Formation of membranes by means of immersion precipitation, Part Ⅱ.The mechanism of formation of membranes prepared from the system CA／acrtone／water, J. Membr. Sci., 1987,34(2): 67
[14]Alltena F W,Smolder C A. Calculation of liquid-liquid phase，seperation inatemary system of a polymer in a mixture of a solvent and nonsolvent, Macromolecules , 1982 ,15 ( 4 ) :1491
[15]Smolder C A, ReuversA J, Boom R M, et al. Microstructures inphase-inversion membranes Part I ,Formation of macrovoids, J. Membr. Sci., 1992 , 73 ( 3 ) :259-275

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com