膜科学与技术

位置：首页 >> 期刊内容阅读

SPEEK/PEI@ILs复合质子交换膜的制备及其PEMWE性能

作者：陈葛锋，王丽华，韩旭彤

单位： 1中国科学院化学研究所，极端环境高分子院重点实验室，北京 100190 2天津工业大学材料科学与工程学院，天津300387

关键词：磺化聚醚醚酮；质子交换膜；电解水制氢；膜电极;质子电导率

DOI号：

分类号： TQ028；TB383

出版年,卷(期):页码： 2023,43(6):29-34

摘要：

以磺化度为75%的磺化聚醚醚酮(SPEEK)为原料，加入聚醚酰亚胺（PEI）和离子液体（ILs）制备SPEEK/PEI@ILs酸碱复合膜用于质子交换膜电解水制氢（PEMWE）中。研究复合膜的吸水率、溶胀度、质子电导率、热稳定性和相应的PEMWE性能。结果表明，SPEEK/PEI@ILs复合膜与商业Nafion117膜相比，具有相近的质子电导率和溶胀度，说明PEI的加入，增强了复合膜的尺寸稳定性。将SPEEK/PEI@ILs复合膜制备成膜电极并测试PEMWE性能，1 A/cm2电流密度下槽电压为2.75V，在0.5A/cm2@1.96V（±0.03）条件下能稳定运行10h。

SPEEK/PEI@ILs acid-base composite membrane was prepared by adding polyetherimide (PEI) and ionic liquid (ILs) to 75% sulfonated poly(ether ether ketone) (SPEEK), which was used in proton exchange membrane water electrolysis to produce hydrogen (PEMWE). The SPEEK/PEI@ILs composite membranes were characterized by FT-IR and SEM, and their water absorption, swelling rate, proton conductivity, thermal stability and mechanical properties were measured. The results show that the SPEEK/PEI@ILs composite membrane has similar proton conductivity and swelling degree compared with the commercial Nafion117 membrane, indicating that the addition of PEI enhances the dimensional stability of the composite membrane. The performance of PEMWE was tested for the SPEEK/PEI@ILs composite membrane and Nafion membranes. The results indicated that the SPEEK/PEI@ILs membrane based MEA could run stably for 10h at 0.5A/cm2@1.96V (±0.03), which would replace Nafion117 membrane in proton exchange membrane electrolysis water hydrogen production and had a better application prospect.

基金项目：

作者简介：

陈葛锋（1997-），男，安徽省安庆市人，硕士，主要研究方向为质子交换膜和膜电极。E-mail：2296729534@qq.com

参考文献：

[1] CHOW J，KOPP R J，PORTNEY P R．Energy resources and global development[J]．Science，2003，302(5650)：1528-1531．
[2] MA Y J，MA Y，WANG Q S，et al．High-entropy energy materials：Challenges and new opportunities[J]．Energy & Environmental Science，2021，14(5)：2883-2905．
[3] PÉREZ G，DÍAZ-SAINZ G，GÓMEZ-COMA L，et al．Rhodium-based cathodes with ultra-low metal loading to increase the sustainability in the hydrogen evolution reaction[J]．Journal of Environmental Chemical Engineering，2022，10(3)：107682．
[4] ULLMAN A N，KITTNER N．Environmental impacts associated with hydrogen production in La Guajira，Colombia[J]．Environmental Research Communications，2022，4(5)：055003．
[5] HERNÁNDEZ-GÓMEZ Á，RAMIREZ V，GUILBERT D，et al．Development of an adaptive static-dynamic electrical model based on input electrical energy for PEM water electrolysis[J]．International Journal of Hydrogen Energy，2020，45(38)：18817-18830．
[6] CHEN J K，LIU H M，HUANG Y A，et al．High-rate roll-to-roll stack and lamination of multilayer structured membrane electrode assembly[J]．Journal of Manufacturing Processes，2016，23：175-182．
[7] PRYKHODKO Y，FATYEYEVA K，HESPEL L，et al．Progress in hybrid composite Nafion®-based membranes for proton exchange fuel cell application[J]．Chemical Engineering Journal，2021，409：127329．
[8] CHEN Y F，GUO H Y，GENG C B，et al．Effect of poly(ether ether ketone) and allyl compounds on microstructure and properties of bismaleimide[J]．Journal of Materials Science：Materials in Electronics，2019，30(2)：991-1000．
[9] ZENG H Z，LI Y B，WANG C W．Using zeolite imidazole frameworks as ionic cross-linkers to improve the performance of composite SPEEK membrane[J]. Sep Purif Technol,2020,236:116258.
[10] HARUN N A M，SHAARI N，NIK ZAIMAN N F H．A review of alternative polymer electrolyte membrane for fuel cell application based on sulfonated poly(ether ether ketone)[J]．International Journal of Energy Research，2021，45(14)：19671-19708．
[11] Tylkowski B. Polymers application in proton exchange membranes for fuel cells (PEMFCs)[J]. Physical Sciences Reviews,2017,2(8):20170018.
[12] KUSOGLU A，TANG Y L，LUGO M，et al．Constitutive response and mechanical properties of PFSA membranes in liquid water[J]．Journal of Power Sources，2009，195(2)：483-492．
[13] GAO S T，XU H L，FANG Z，et al．Highly sulfonated poly(ether ether ketone) grafted on graphene oxide as nanohybrid proton exchange membrane applied in fuel cells[J]．Electrochimica Acta，2018，283：428-437．
[14] KHAN M I，SHANABLEH A，SHAHIDA S，et al．SPEEK and SPPO blended membranes for proton exchange membrane fuel cells[J]．Membranes，2022，12(3)：263．
[15] DA TRINDADE L G，BORBA K M N，ZANCHET L，et al．SPEEK-based proton exchange membranes modified with MOF-encapsulated ionic liquid[J]．Materials Chemistry and Physics，2019，236：121792．
[16] SULTAN A S，AL-AHMED A，JAVAID ZAIDI S M．Reduced viscosity，rheology and morphological properties of sulfonated poly (ether ether ketone)：Polyetherimide blends[J]．European Polymer Journal，2011，47(12)：2295-2302．
[17] 孙佳雯，王丽华，韩旭彤．掺杂纤维素/离子液体的聚苯并咪唑质子传导膜及钒电池性能研究[J]．膜科学与技术，2022，42(4)：43-50，58．
[18] LIU S A，WANG L H，DING Y E，et al．Novel sulfonated poly (ether ether keton)/polyetherimide acid-base blend membranes for vanadium redox flow battery applications[J]．Electrochimica Acta，2014，130：90-96．
[19] 李丹．SPEEK/GO系列质子交换膜的制备及钒电池应用[D]．天津：天津工业大学，2016．

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com